Bambu Lab PETG HF (Refill)
PETG HF (High Flow) filament is a fully optimised PETG filament designed specifically for high-speed printing. With a default printing speed that is twice as fast as standard PETG filaments, PETG HF takes your printing efficiency to new heights.
It effectively addresses common issues such as oozing and clumping associated with regular PETG, ensuring smoother and more reliable prints. The new matte finish not only enhances the aesthetic by smoothing out uneven gloss during speed transitions but also provides a consistently uniform look.
Offering greater durability and toughness than PLA, PETG HF is the ideal choice for creating long-lasting items with an improved finish and faster production times.
Tips: To learn about using this filament refill with Bambu Reusable Spool on Bambu Lab Wiki, click here.
Recommended Printing Settings
| Drying Settings before Printing | 65 °C, 8 h |
| Printing and Keeping Container's Humidity | < 20% RH (Sealed, with Desiccant) |
| Nozzle Temperature | 230 - 260 °C |
| Bed Temperature (with PVP Glue) | 65 - 75 °C |
| Printing Speed | < 300 mm/s |
Physical Properties
| Density | 1.28 g/cm³ | |
| Vicat Softening Temperature | 70 °C | |
| Heat Deflection Temperature | 69 °C | |
| Melting Temperature | 214 °C | |
| Melt Index | 28.2 ± 2.7 g/10 min |
Mechanical Properties
| Tensile Strength | 34 ± 4 MPa |
| Breaking Elongation Rate | 8.6 ± 1.2 % |
| Bending Modulus | 2050 ± 120 MPa |
| Bending Strength | 64 ± 3 MPa |
| Impact Strength | 31.5 ± 2.2 kJ/m² |
Original: $23.04
-70%$23.04
$6.91More Images
Bambu Lab PETG HF (Refill)
PETG HF (High Flow) filament is a fully optimised PETG filament designed specifically for high-speed printing. With a default printing speed that is twice as fast as standard PETG filaments, PETG HF takes your printing efficiency to new heights.
It effectively addresses common issues such as oozing and clumping associated with regular PETG, ensuring smoother and more reliable prints. The new matte finish not only enhances the aesthetic by smoothing out uneven gloss during speed transitions but also provides a consistently uniform look.
Offering greater durability and toughness than PLA, PETG HF is the ideal choice for creating long-lasting items with an improved finish and faster production times.
Tips: To learn about using this filament refill with Bambu Reusable Spool on Bambu Lab Wiki, click here.
Recommended Printing Settings
| Drying Settings before Printing | 65 °C, 8 h |
| Printing and Keeping Container's Humidity | < 20% RH (Sealed, with Desiccant) |
| Nozzle Temperature | 230 - 260 °C |
| Bed Temperature (with PVP Glue) | 65 - 75 °C |
| Printing Speed | < 300 mm/s |
Physical Properties
| Density | 1.28 g/cm³ | |
| Vicat Softening Temperature | 70 °C | |
| Heat Deflection Temperature | 69 °C | |
| Melting Temperature | 214 °C | |
| Melt Index | 28.2 ± 2.7 g/10 min |
Mechanical Properties
| Tensile Strength | 34 ± 4 MPa |
| Breaking Elongation Rate | 8.6 ± 1.2 % |
| Bending Modulus | 2050 ± 120 MPa |
| Bending Strength | 64 ± 3 MPa |
| Impact Strength | 31.5 ± 2.2 kJ/m² |
Product Information
Product Information
Shipping & Returns
Shipping & Returns
Description
PETG HF (High Flow) filament is a fully optimised PETG filament designed specifically for high-speed printing. With a default printing speed that is twice as fast as standard PETG filaments, PETG HF takes your printing efficiency to new heights.
It effectively addresses common issues such as oozing and clumping associated with regular PETG, ensuring smoother and more reliable prints. The new matte finish not only enhances the aesthetic by smoothing out uneven gloss during speed transitions but also provides a consistently uniform look.
Offering greater durability and toughness than PLA, PETG HF is the ideal choice for creating long-lasting items with an improved finish and faster production times.
Tips: To learn about using this filament refill with Bambu Reusable Spool on Bambu Lab Wiki, click here.
Recommended Printing Settings
| Drying Settings before Printing | 65 °C, 8 h |
| Printing and Keeping Container's Humidity | < 20% RH (Sealed, with Desiccant) |
| Nozzle Temperature | 230 - 260 °C |
| Bed Temperature (with PVP Glue) | 65 - 75 °C |
| Printing Speed | < 300 mm/s |
Physical Properties
| Density | 1.28 g/cm³ | |
| Vicat Softening Temperature | 70 °C | |
| Heat Deflection Temperature | 69 °C | |
| Melting Temperature | 214 °C | |
| Melt Index | 28.2 ± 2.7 g/10 min |
Mechanical Properties
| Tensile Strength | 34 ± 4 MPa |
| Breaking Elongation Rate | 8.6 ± 1.2 % |
| Bending Modulus | 2050 ± 120 MPa |
| Bending Strength | 64 ± 3 MPa |
| Impact Strength | 31.5 ± 2.2 kJ/m² |